What epoxy
Posted by:
William Warneri
(---.12.159.143.dyn.plus.net)
Date: January 16, 2020 06:35PM
Which epoxy finish would anyone recommend rod dancer u 40 flexcoat etc and why
I'm building a twin tip barbel rod on a harrisons blank (1.5lb/2.0lb) Re: What epoxy
Posted by:
Tom Kirkman
(Moderator)
Date: January 16, 2020 07:18PM
They are all equally good. The idea that any one particular finish is better than another is bunk. But they each have their own unique characteristics. Find the one that suits you best and stick with it. This requires some experimentation on your part.
There are no bad epoxies. Only bad epoxiers.... Re: What epoxy
Posted by:
Ken Brown 2
(---.229.247.206.res-cmts.sm.ptd.net)
Date: January 17, 2020 07:15AM
Its all about preference and application. I have tried several and they all equally work well. Its all about the 'epoxier' as Tom put it. If you like a single coat epoxy, use that. If you like a light build epoxy, medium..blah blah..you get the idea. Re: What epoxy
Posted by:
William Warneri
(213.205.242.---)
Date: January 17, 2020 09:21AM
Thank you gentlemen Re: What epoxy
Posted by:
William Giokas
(---)
Date: January 24, 2020 01:32PM
I use Flex coat and heat it in the microwave before I apply it. About 30 seconds is all it takes to make the Flexcoat flow smoothly. However, you must work quickly as heating any epoxy makes it work faster. Bill Sorry, only registered users may post in this forum.
|